Lumix-3D Zirconia

E lemohile gradient ea tlhaho ea 'mala, translucency le matla ka kutloisiso ea' nete .

Ho hanyetsa botsofali bo phahameng le matla a phahameng ho fihla ho li-unit tsa 14 borokho

Phetoho ea tlhaho ea Multilayer e ka lumellana le phetoho ea 'mala oa leino la tlhaho ho tloha ho incisal ho ea ho cervical.

Ts'ehetso ea Bloomden chairside fast sintering system e ka qeta ho sintering ka 66 Minutes.

ikopanye Joale

Ha ho bapisoa le sethaleng se fetileng matla e le mokhoa

Bloomden^②Lumix-3D ha e tšoane le zirconia leha e le efe, e ka bonts'a matla a mangata ho tloha ho 800MPa ho ea ho 1200MPa e ka koahelang li-posteriors le li-anteriors bakeng sa meqhaka le marokho ka bobeli ho kenyeletsa ho tsosolosa ho kenngoa.
Phetoho ea tlhaho e kang bophelo

E lemohile natur al gradient ea mebala, translucency le matla ka kutloisiso ea 'nete. Sekhahla sena se kang bophelo se finyelloa ka mokhoa o bitsoang "color grading", o kenyelletsang ho kopanya mebala e fapaneng ea zirconia ho theha phello ea tlhaho. Phello ke lets'oao la meno le ts'oanang hantle le ponahalo ea meno a tlhaho, a etsa hore a khethollehe ho meno a potolohileng ho latela 'mala le sebopeho.
VITA e tsitsitseng^®Papali ea Moriti oa khale

Re fana ka 'mala o ikhethang oa mebala bakeng sa mefuta eohle ea VITA ea mefuta e 16, ho kenyeletsoa BL2. Boleng ba rona bo lumellana ho pholletsa le lihlopha, 'me litsebi tsa meno tsa Europe le USA li tiisitse ho nepahala ha mebala ea rona.
High-Speed sintering e etsa mosebetsi o atlehileng haholoanyane

Bloomden e fana ka tharollo e khethehileng bakeng sa ho fihlella sintering ka lebelo le phahameng ka nako e behiloeng ea metsotso e 63 ka ho kopanya li-curve tse ikhethang le lisebelisoa tse sebetsang tsa sintering.

Lipontšo tse khothalelitsoeng

Lintlafatso li fumaneha ka meqhaka e felletseng ea li-contour tsa monolithic, marokho, li-veneers kapa arch e felletseng.

Veneer
Anterior Crown
Moqhaka o ka morao
Inlay
Borokho bo felletseng ba Crown
Moqhaka oa Impant
Kenya Arch e felletseng
Borokho bo felletseng ba arch

Sintering Curve

tlhalosege

3-8 diyuniti

≥9 diyuniti

Technical tobileng

Lumix-3D
ZrO2+Hf02+Y203	≥98%
Y203	4.5% -8.0%
Density Before Sintering(g.cm-3)	3.15 ± 0.05
Tekano ka Mora ho Sintering(g.cm-3)	6.07 ± 0.01
CTE (25-500℃C)(K-1)	10.5 ± 0.5
Flexural Strength After Sintering (MPa)	800-1200
Litaba tsa Monoclinic Phase ea botsofali
Phetoho ea Leseli
Ho qhibiliha ha Lik'hemik'hale Ka mor'a ho Sintering(ug.cm-2)
Cytotoxicity	0 Tloha
Radioactivity(Bq.g-1)
Sintering Temperature(℃C)	1480
Systems	98mm/95mm/92*75mm
botenya	12m/14mm/16mm/18mm20mm/22mm/25mm/30mm
Mekha	A1 A2 A3 A3.5 A4/B1 B2 B3 B4C1 C2 C3 C4/D2 D3 D4/BL1 BL2 BL3 BL4

Testimonials

Ke 'nile ka sebelisa theknoloji ea sintering ea zirconia ka likhoeli tse' maloa joale, 'me ke thabetse liphello. Ts'ebetso ea sintering e potlakileng e fokolitse haholo nako e hlokahalang ho hlahisa tsosoloso ea boleng bo phahameng ba zirconia, e ntumellang ho nka mosebetsi o mongata le ho eketsa tlhahiso ea ka. Matla le aesthetics ea tsosoloso e ntle feela, haeba e se betere, ho feta mekhoa ea setso ea sintering, 'me bakuli ba ka ba khotsofetse haholo ka liphello. Ke ananela ho fokotsoa ha tšebeliso ea matla , e leng se etsang hore ts'ebetso e be le tikoloho.

Ka kakaretso, theknoloji ea sintering ea zirconia e fetohile phetoho ea lipapali bakeng sa lab ea ka, 'me ke tla e khothaletsa haholo ho setsebi leha e le sefe sa meno se batlang ho ntlafatsa ts'ebetso ea bona ea mosebetsi le boleng ba tlhahiso.